Sand casting

Sand casting, which in a general sense involves the forming of a casting mold with sand, includes conventional sand casting and evaporative pattern (lost-foam) casting.

In conventional Sand casting, the mold is formed around a pattern by ramming sand, mixed with the proper bonding agent, onto the pattern. Then the pattern is removed, leaving a cavity in the shape of the casting to be made. If the casting is to have internal cavities or undercuts, sand cores are used to make them. Molten metal is poured into the mold, and after it has solidified the mold is broken to remove the casting. In making molds and cores, various agents can be used for bonding the sand. The agent most often used is a mixture of clay and water.

Casting quality is determined to a large extent by foundry technique. Proper metal-handling practice is necessary for obtaining sound castings. Complex castings with varying wall thickness will be sound only if proper techniques are used.

Evaporative (lost-foam) pattern casting
Evaporative pattern casting (EPC) is a sand casting process that uses an unbounded sand mold with an expendable polystyrene pattern placed inside of the mold. This process is somewhat similar to investment casting in that an expendable material can be used to form relatively intricate patterns in a surrounding mold material. Unlike investment casting, however, evaporative pattern casting (EPC) involves a polystyrene foam pattern that vaporizes during the pouring of molten metal into a surrounding mold of unbounded sand.

Shell Mold Casting
In shell mold casting, the molten metal is poured into a shell of resin-bonded sand only 10 to 20 mm thick - much thinner than the massive molds commonly used in sand foundries. Shell mold castings surpass ordinary sand castings in surface finish and dimensional accuracy and cool at slightly higher rates; however, equipment and production are more expensive.

Plaster Casting
In this method, either a permeable (aerated) or impermeable plaster is used for the mold. The plaster in slurry form is poured around a pattern, the pattern is removed and the plaster mold is baked before the casting is poured. The high insulating value of the plaster allows castings with thin wads to be poured.

Minimum wall thickness of aluminum plaster castings typically is 1.5 mm. Plaster molds have high reproducibility, permitting castings to be made with fine details and close tolerances. Mechanical properties and casting quality depend on alloy composition and foundry technique. Slow cooling due to the highly insulating nature of plaster molds tends to magnify solidification-related problems, and thus solidification must be controlled carefully to obtain good mechanical properties.

Cost of basic equipment for plaster casting is low; however, because plaster molding is slower than sand molding, cost of operation is high. Aluminum alloys commonly used for plaster casting are 295.0, 355.0, C355.0, 356.0 and A356.0.

Investment casting
Investment casting of aluminum most commonly employs plaster molds and expendable patterns of wax or other fusible materials. Plaster slurry is "invested" around patterns for several castings, and the patterns are melted out as the plaster is baked.

Investment casting produces precision parts; aluminum castings can have walls as thin as 0.40 to 0.75 mm. However, investment molding is often used to produce large quantities of intricately shaped parts requiring no further machining so internal porosity seldom is a problem. Because of porosity and slow solidification, mechanical properties are low.

Investment casting usually are small, and it is especially suited to production of jewelry and parts for precision instruments. Recent strong interest by the aerospace industry in the investment casting process has resulted in limited use of improved technology to produce premium quality castings. Combining this accurate dimensional control with the high and carefully controlled mechanical properties can, at times, justify casting costs and prices normally not considered practical.

Aluminum alloys commonly used for investment castings are 208.0, 295.0, 308.0, 355.0, 356.0, 443,0, 514.0, 535.0 and 712.0.

Centrifugal Casting
Centrifuging is another method of forcing metal into a mold. Steel baked sand, plaster, cast iron, or graphite molds and cores are used for centrifugal casting of aluminum. Metal dies or molds provide rapid chilling, resulting in a level of soundness and mechanical properties comparable or superior to that of gravity-poured permanent mold castings.

Wheels, wheel hubs, and papermaking or printing rolls are examples of aluminum parts produced by centrifugal casting. Aluminum alloys suitable for permanent mold, sand, or plaster casting can be cast centrifugally.

Continuous Casting
Long shapes of simple cross section (such as round, square, and hexagonal rods) can be produced by continuous casting, which is done in a short, bottomless, water-cooled metal mold.

The casting is continuously withdrawn from the bottom of the mold; because the mold is water cooled, cooling rate is very high. As a result of continuous feeding, castings generally are free of porosity. In most instances, however, the same product can be made by extrusion at approximately the same cost and with better properties, and thus use of continuous casting is limited. The largest application of continuous casting is production of ingot for rolling, extrusion, or forging.

Composite-Mold Casting
Many of the molding methods described above can be combined to obtain greater flexibility in casting. Thus, dry sand cores often are used in green sand molds, and metal chills can be used in sand molds to accelerate local cooling.